Design and use:
Type DP110
- short processing time (8 - 10 minutes)
- after a short time the first load on the joined parts is possible
- viscoplastic
- high shear strength (18 MPa)
- good peel strength (35 N/cm), impact resistance and ageing properties
- made of epoxy resin
- low flow rate
- hand-proof after approx. 20 minutes
- application temperature -55 °C up to +80 °C
- for bonding metals, plastics like ABS, GRP, PC etc. and other materials
- suitable mixing nozzle: 9560150021

Type DP490
- very long processing time (more than 90 minutes)
- thixotropic = does not flow on vertical surfaces
- viscoplastic
- high shear strength (30 MPa)
- good peel strength (92 N/cm) and impact resistance
- based on epoxy resin
- hand-proof after approx. 4 hours
- application temperature from -55 °C up to +120 °C
- temperature resistance 120 °C
- for bonding metals like aluminium, steel or brass, plastics like ABS, PA, PC, rigid PVC etc. as well as fibre composite materials
- suitable mixing nozzle: 9560150021

Type DP8005
- very short processing time (2 - 3 minutes)
- fast accumulation of strength
- bonding of low-energy plastics without pretreatment of surfaces
- after a very short time the first load on the joined parts is possible
- viscoplastic
- high shear strength (6 MPa)
- good peel strength (28 N/cm) and impact resistance
- made of acrylate
- low flow rate
- hand-proof after approx. 30 minutes
- application temperature from -55 °C up to +80 °C
- for bonding PE, PP and TPE as well as ABS, hard PVC, PMMA, fibre composites, lacquered and primed metals, glass, wood etc.
- suitable mixing nozzle: 9560150022